配分工艺对中碳Ti-Mo高强Q&P钢组织和性能的影响

摘要：采用盐浴实验、扫描电镜、透射电镜、拉伸实验和磨损实验等手段，研究了配分工艺对中碳Ti Mo钢组织和性能的影响，分析了不同配分工艺处理下的组织演变和性能变化。结果表明，显微组织主要由回火马氏体、渗碳体、(Ti，Mo)C粒子组成。随着配分时间的延长和配分温度的升高，板条马氏体数量减少，马氏体板条厚度增加，边界钝化。此外，随着配分温度从310℃提高至400℃，抗拉强度、硬度和低温冲击韧性同时下降，分别降低约250MPa、56HV和15J。最后，Ms以下温度配分（310℃）试样的耐磨损性能明显优于Ms以上温度配分（400℃）试样。Ms以下温度配分试样磨损表面形貌以塑性变形为主，Ms以上温度配分试样磨损表面以犁沟为主。     

活性焦法烧结烟气脱硫率影响因素统计解析

摘要：为明确影响活性焦烧结烟气脱硫的主要因素，通过模拟试验和生产数据统计分析探究脱硫塔自上至下脱硫率变化趋势和各运行参数对脱硫率的影响。模拟试验表明，循环使用后的活性焦孔隙结构更加发达，表面含氧官能团含量增加，进而其初期脱硫性能低于新鲜活性焦，后期优于新鲜活性焦。错流式脱硫塔自上至下脱硫率先后经历100%、快速降低、缓慢降低等过程。生产数据统计分析表明，脱硫率与SO2质量浓度、O2体积分数、H2O体积分数、NH3与NOx物质的量之比、解析温度呈正相关，与活性焦床温度、体积空速呈负相关。其中，SO2质量浓度、体积空速、活性焦床温度对脱硫率影响最大。运行参数之间存在多重共线性现象，烧结漏风率升高或空气补加量增加将引起诸多运行参数的变化，但总体上有利于脱硫率的提高。     

Effect of Temperature and Strain Rate on the Hot Deformation Behaviour of Ferritic Stainless Steel

Metals and Materials International - The flow behaviour and microstructure characteristics of a ferritic stainless steel were investigated using plain strain compression test on a Gleeble 3500...     

废脱硫剂在铁矿烧结中的应用

钢厂煤气脱硫工序排放的废脱硫剂是一种难以利用的有害固体废弃物，含一定量的铁及较高的钙和硫等元素。对废脱硫剂配入铁矿粉中进行了烧结杯的试验研究，结果表明，当废脱硫剂配比超过01%后，随着废脱硫剂配比的升高，烧结矿转鼓强度下降，利用系数下降，烧结烟气中SO2与NOx浓度增加，烧结矿的还原度有所下降，但烧结矿的低温还原粉化性能有所改善。烧结矿的矿相研究发现，废脱硫剂配比偏大时，磁铁矿体积分数增大，铁酸钙体积分数减少，并由针状结构向柱状、板状演变，烧结矿的气孔率上升。主要原因在于其粒度偏粗，含硫高，不利于成矿。当废脱硫剂粒度为-63mm及其配比控制在01%时，烧结矿的产量和质量有所改善，烟气中SO2、NOx较基准试验变化不大。工业试验表明，在烧结混匀矿中配入废脱硫剂配比小于012%时，烧结矿产量和质量没有明显变化，烧结烟气脱硫脱硝效果也没有受到影响。废脱硫剂掺入铁矿中进行烧结是一种资源化利用的有效方法，不仅解决了有害固体废弃物对环境的影响，而且使二次资源得到综合利用。     

电工钢磁性检测方法国家标准应用问题和解决方案

通过对电工钢交流磁性检测方法现行国家标准（爱泼斯坦方圈法和标准单片法）在应用中存在的问题进行了梳理和解析，认为主要问题包括次级电压波形失真时需修正比总损耗、约定的有效磁路长度并非实际有效磁路长度以及磁性测量系统校准方法缺失等，并提出了采用数字反馈控制技术控制次级电压波形无需修正比总损耗、取向硅钢单片法测量时采用475 mm有效磁路长度以及磁性测量系统综合校准方案等一些解决方案。     

高炉炉缸凝铁层的组成分析与导热系数测定

摘要：高炉炉缸内衬表面形成稳定的凝铁层将保护高炉炭砖并延长高炉寿命。利用光学数码显微镜观察统计分析高炉凝铁层生产样品，探究不同焦炭体积占比对凝铁层导热系数的影响。利用元素分析（XRF）、X射线衍射分析（XRD）、扫描电镜(SEM-EDS)等手段分析凝铁层的组成，并观察其微观形貌。利用瞬态平面热源法（TPS）测定凝铁层的导热系数，进一步分析其组成与导热系数之间的关系。结果表明,凝铁层由铁、充满铁水的焦炭、石墨碳、少量渣相组成，凝铁层内部没有气隙。凝铁层生产样品的导热系数测定范围为27.21～97.38W/(m·K)，导热系数（λ）与其组成的焦炭面积比（Sc=22%～48%）之间的线性关系为：λ=-257.47Sc +157.65。模拟实验凝铁层的导热系数范围为30.54～53.95W/(m·K)，该值远大于目前数学模型中采用的凝铁层导热系数（2～4W/m·K），随着焦炭粒度的增加，凝铁层的导热系数先增加后减小。凝铁层中导热系数（λ）与焦炭体积分数Vc（Vc=39%～50%）的线性关系为：λ=-80.50Vc +78.56。研究结果进一步明确了凝铁层的物相组成及其导热系数，为高炉长寿的研究指明了方向。     

Investigation of separation phenomenon in high-toughness X70 thick-walled linepipe steel

Separation is a commonly observed phenomenon during drop weight tear testing in high-toughness linepipe steels. Severe separation is harmful because it may cause fracturing or bursting of pipes. In this study,a quantitative measurement of separation was proposed,and using this new method,a relationship between the separation and microstructure was determined and discussed. The microstructures observed using optical and scanning electron microscopy revealed that the separation was related to the mixed ferritic and bainitic microstructures,or rather,it was related to the carbon enrichment in bainite.     

Effect of grinding-induced cyclic heating on the hardened layer generation in the plunge grinding of a cylindrical component

This paper discusses the effects of the grinding-induced cyclic heating on the properties of the hardened layer in a plunge cylindrical grinding process on the high strength steel EN26. It was found that a multi-pass grinding brings about a uniform and continuous hardened layer along the circumference of the cylindrical workpiece. An increase of the number of grinding passes, leads to a thicker layer of hardening, a larger compressive residual stress and a deeper plastic deformation zone. Within the plastic deformation zone, the martensitic grains are refined by the thermo-mechanical loading, giving rise to a hardness of 12.5% higher than that from a conventional martensitic transformation. The coupled effects of heat accumulation and wheel wear in the multi-pass grinding are the main causes for the thickening of the hardened layer. A too small infeed per workpiece revolution would result in insufficient grinding heat, and in turn, bring about an undesirable tempered hardened layer and a reduction of its hardness.     

Modelling and optimisation of biomass injection in ironmaking blast furnaces

Biomass is a renewable and potentially carbon-neutral energy source and can be a promising alternative to fossil fuels in the ironmaking industry. Pulverised biomass injection (PBI) is the most promising technology to use biomass-based materials in ironmaking blast furnaces (BFs). This paper reviews key aspects of recent research relating to biomass combustion in the raceway region: experimental studies, numerical studies, and the application of the research findings to optimise BF practice. In the experimental part, the pretreatment of raw biomass to produce pyrolysed biochar products for improving applicability in BFs is reviewed. The properties of raw biomass and biochar are compared with the main requirements for injection into BFs, and the process tests that have been employed at lab- and pilot-scales are reviewed. In the modelling part, a comprehensive overview of mathematical modelling of biomass combustion in BFs is presented, ranging from turbulent flow to heat transfer and mass transfer, as well as key reaction models for simulating the lower part of the BF. With respect to the application of the research, in-furnace phenomena understanding, operation optimisation, and facility design are reviewed, including the co-firing of biomass and coal. In addition, heat and mass balance modelling has been used to demonstrate the operating window of feasible operations using PBI. Life cycle assessment has been reviewed to demonstrate PBI's environmental credentials. Based on the aspects reviewed, conclusions have been drawn on the strengths, limitations, and outlook of PBI studies. This paper offers a comprehensive review of the combustion of biomass in BFs and should prove useful for process understanding, design and optimisation towards green ironmaking technology.     

附加外场力对锌锅表层锌液流动和锌渣分布的影响

实测了热镀锌锌锅表层锌液的流速,并分析了锌锅浮渣的分布特点,提出了一种在锌锅锌液上方主动加载外场力作用以驱动锌液流动进而改变锌渣分布的新方法,称为锌渣流动管理方法(DFMS-Dross Flowing Management System)。通过源力加载的方式修正了流体动量守恒方程,建立了锌液流场数值计算模型,模拟了不同外场力加载布局下锌锅表层锌液的流场。结果表明,附加外场力作用可有效促进锌锅表层锌液的切向流动,最大切向流速可达0.8 m/s;表层锌液的切向流动可拖动锌渣跟随流动,进而改变锌渣分布,促进锌锅排渣,证实了DFMS的有效性。模拟结果还表明,锌锅表层锌液的切向流速受外场力加载时间的影响较小,而随加载外场力的增大而增大,但加载外场力的大小对100~200 mm深锌液的流速影响较小。最后,通过定义锌锅表层锌液的排渣时间因子讨论了不同外场力加载方式的排渣效率。